Application analysis of PTFE coating

Fluorine resin coating was born as early as 1938, the earliest fluorine carbon coating is Dupont Teflon coating that is PTFE copolymer, this kind of material has unique excellent heat resistance, low temperature resistance, self-lubrication and chemical stability, etc., but this kind of coating requires a very high liquefaction temperature when used, the dispersion of the pigment is also poor, so the initial application range is narrow.

The applications of PTFE coating
Because PTFE coating has the above excellent performance, it has been used in non-stick pan, aviation, medical and other fields. Waterborne coatings are used in laser printers, such as fuser films.The coating on fuser film has good high temperature resistance, which is installed on the heating component, working temperature can reach 200 ℃. Due to its surface tension generally only 31 ~ 34 dyne/cm, low surface energy, the contact angle is large, adhesive does not sufficiently wet the coating, thus cannot very good adhesion, so the coating with excellent non-stick properties, not easy to stick carbon powder, non stick dust scale, anti-fouling is good. PTFE coating swelling and dissolving are more difficult than an amorphous polymer , due to good chemical stability, it has excellent anti-corrosion property, good chemical inertness, paint film, acid, alkali, salt and other chemicals and a variety of chemical solvents, provide protection barrier for base material; Paint film surface toughness, high strength; Coating wear-resisting performance is excellent, print number of ordinary paper generally in more than 50000 pcs; Additionally, waterborne PTFE coating is a kind of environmental protection coating, less pollution to the environment and coating equipment easy to clean, the general defects such as impurities can be identified before baking and re-processing, to a certain extent improve product qualification rate; The pigment dispersion performance of waterborne PTFE coating is poor than solvent-based coating, easy to produce stratification; This type of coating baking temperature is higher, baking surface temperature is generally 360 ~ 400 ℃. Because of PTFE high melting point, it need to introduce better affinity resin, on the basis of performance does not harm the resin itself to improve its adhesion, therefore appeared in the paint, coatings, primer, also have a paint. These varieties of form a complete set of coating is solved the above problems.

Appear on the market of coating with PTFE resin, it has excellent non-sticky, corrosion resistance, weathering resistance, low friction performance. Meanwhile, because of the existence of the hydrocarbon chain hydrocarbon composition of different functional groups and show some solubility, crosslinking, wetting, adhesion and flow property, it’s important that it overcome the performance before cannot be cured at room temperature, therefore, it can be used as the preparation of building exterior wall coating resin. It is weather-resistant and self-cleaning when applied, and has a long life and does not fade and so on; At the same time it also apply to the anti corrosion of metal components, especially suitable for harsh environment under the condition of acid and alkali resistant and corrosion resistant coating and various transport antioxidant tool shell coating, such as cars. Automobile industry has entered the stage of total higher steady development. Such kind of coatings in the automotive industry a wide range of applications, not only can provide more excellent performance, can also through modification, the measure such as recycling waste paint in a certain extent, reduce the pollutant emissions, reduce the pollution of the environment. Car sales are a fluorine resin paint in recent years, the excellent properties of PTFE resin is more and more cars make people attention, fully embodies its huge potential use value.

PTFE coating has been drawn increasingly attention by people, it is widely used in petroleum, chemical, mechanical, aviation, aerospace, nonferrous metals, electronics and other economic construction. In recent years, people through its modification, to broaden its scope of application, reducing the use of restrictions. Because of its non-stick, high and low temperature resistance and resistance to friction and corrosion, I believe that in the near future, it can be more extensive in the field play a more amazing role.

If you need more information about our products, please contact us: ,our engineers will answer you and provide free samples.

pdfApplication analysis of PTFE coating.pdf